4C™ Table Summary
Laboratory and Field Tests Summary: Shooter Solutions’ 4C™ (Non-Hot Process)
|
Scale |
Target Metal |
Purpose |
Results |
|
|
Field test |
Steel |
Powder Coating |
Passed all required quality tests. Also, passed 1500 hours of salt spray test in both cases (ASTM B117). Test also shows Zero Creepage. |
|
|
Field test |
Aluminum |
Powder Coating |
Passed all quality tests with 500 hours of salt spray test |
|
|
Commercial operation |
Steel and Aluminum |
Powder Coating & Liquid painting |
All quality requirements, along with a reduction of around 50% on process time with respect to alternative and running cost. Zero rejection in one year. It also works for High Temp Metal coatings that now are applied onto bare metal. |
|
|
Lab Test |
Steel |
Painting |
Passed 1540 hours of salt spray test with minimum surface preparation. Where it failed at only the exposed edges, no rust creeping occurred. (ASTM B117) |
|
|
Lab Test |
Aluminum |
Anodizing |
Passed 500 hours of salt spray test with minimum surface preparation (ASTM B117) |
|
|
US EPA Evaluation & Testing |
Steel |
Hard Chrome Plating |
This technology passed preliminary quality tests |
|
|
US EPA Evaluation & Testing |
Aluminum |
Sulfuric Acid Anodizing (Type II Class 1) |
This technology passed 500 hours of salt spray test (ASTM B117). |
WELDING TESTS :
|
General Motors Corp. |
Evaluation & Testing |
Steel |
Spot Welding |
Showed 60 % increase in weld strength |
|
PSI , Inc. Previously known as Pittsburgh Testing Lab. |
Lab Test |
Hot & Cold rolled Steel |
Fillet Welding |
|
BACK (To 4C™ FAQ.)
Encrypted Secure Order Cart Payment Options: 
Checks made out to Shooter Solutions, 1910 Burk Rd, Suite 103, Blaine WA 98230
1-800-354-2022 orders only, technical help 1-360-354-2022 and e-mail
help@shootersolutions.com?subject=help me